FCAW wire for 18%Cr — 12%Ni – 3% Mo- N stainless steel For all-position welding.Recommended for welding type 317 stainless steel to give a maximum of 0.04% carbon in the weld deposit. The higher molybdenum content, as compared to type 316L, further reduces susceptibility to pitting corrosion. Used in the pulp and paper industry and in other severe corrosion applications involving sulfuric and sulfurous acids and their salts.

Загрузка...

Описание

FCAW wire for 18%Cr — 12%Ni – 3% Mo- N stainless steel For all-position welding.Recommended for welding type 317 stainless steel to give a maximum of 0.04% carbon in the weld deposit. The higher molybdenum content, as compared to type 316L, further reduces susceptibility to pitting corrosion. Used in the pulp and paper industry and in other severe corrosion applications involving sulfuric and sulfurous acids and their salts.



Типичные свойства образца с V-образным надрезом по Шарпи

после сварки c1 shielding gas

Механические свойства при растяжении

Состояние После сварки После сварки
Защитный газ M21 Shielding gas C1 Shielding Gas
Предел прочности при растяжении 620 MPa (90 ksi) 600 MPa (87 ksi)
Предел текучести 480 MPa (70 ksi) 460 MPa (67 ksi)
Удлинение 35 % 34 %

Классификации

Weld Metal SFA/AWS A5.22 : E317LT1-1(4)
JIS Z 3323 : YF317LC
KS D 3612 : YF317LC

Характеристики расходного материала

Тип сплава C Cr Ni Mo
Защитный газ M21, C1 (EN ISO 14175)
Сварочный ток DC+

Хим. состав наплавленного металла

Хим. состав наплавленного металла
C Cr Mn Mo Ni P S Si
C1 Shielding Gas
18.4 % 3.40 % 0.021 % 0.009 %
C1 Shielding gas
12.5 %
C1 shielding Gas
0.032 %
C1 shielding gas
1.20 % 0.80 %
M21 Shielding Gas
1.20 % 13.0 %
M21 Shielding gas
0.032 % 19.50 % 3.50 % 0.021 % 0.009 %
M21 shielding gas
0.85 %