FCAW wire for 22%Cr — 12%Ni stainless steel, For all-position welding. Designed for welding type 309 wrought or cast forms, but used extensively for welding type 304 to mild or carbon steel. Also used for welding 304 clad sheets and for applying stainless steel sheet linings to carbon steel. Carbon content 0.04% maximum.

Загрузка...

Описание

FCAW wire for 22%Cr — 12%Ni stainless steel, For all-position welding. Designed for welding type 309 wrought or cast forms, but used extensively for welding type 304 to mild or carbon steel. Also used for welding 304 clad sheets and for applying stainless steel sheet linings to carbon steel. Carbon content 0.04% maximum.



Типичные свойства образца с V-образным надрезом по Шарпи

после сварки c1 shielding gas

Механические свойства при растяжении

Состояние После сварки После сварки
Защитный газ M21 Shielding Gas C1 Shielding gas
Предел прочности при растяжении 600 MPa (87 ksi) 539 MPa (78 ksi)
Предел текучести 480 MPa (70 ksi) 392 MPa (57 ksi)
Удлинение 35 % 51 %

Данные наплавки

Ток 130-220 A
Коэфф. наплавки 4.2-10. lb/h
Коэфф. наплавки 1.9-4.6 kg/h
Диаметр 0.045 in.
Диаметр 1.2 mm
В 24-29 V
Скорость подачи проволоки 228-567 in./min
Скорость подачи проволоки 5.8-14.4 m/min

Классификации

Weld Metal SFA/AWS A5.22 : E309LT1-4
SFA/AWS A5.22 : E309LT1-1
KS D 3612 : YF-309LC
EN ISO 17633-A : T 23 12 L P C1 2
EN ISO 17633-A : T 23 12 L P M21 2
JIS Z 3323 : YF-309LC

Характеристики расходного материала

Тип сплава C Cr Ni
Защитный газ M21, C1 (EN ISO 14175)
Сварочный ток DC+

Хим. состав наплавленного металла

Хим. состав наплавленного металла
C Cr Mn Ni P S Si
C1 Shielding Gas
0.029 % 0.024 % 0.007 %
C1 Shielding gas
23.1 % 12.4 %
C1 shielding gas
1.10 % 0.80 %
M21 Shielding Gas
0.030 % 23.5 % 1.30 % 12.5 % 0.024 % 0.007 % 0.90 %