FCAW wire for dissimilar metals, For all-position welding.Designed for welding type 316 clad steels on the first pass in cladding steels or for welding dissimilar metals such as Mo-containing austenitic stainless steels to carbon steels. Used in paper mills and in power plants. Carbon content 0.04% maximum.

Загрузка...

Описание

FCAW wire for dissimilar metals, For all-position welding.Designed for welding type 316 clad steels on the first pass in cladding steels or for welding dissimilar metals such as Mo-containing austenitic stainless steels to carbon steels. Used in paper mills and in power plants. Carbon content 0.04% maximum.



Типичные свойства образца с V-образным надрезом по Шарпи

после сварки c1 shielding gas

Механические свойства при растяжении

Состояние После сварки После сварки
Защитный газ M21 Shielding Gas C1 Shielding Gas
Предел прочности при растяжении 750 MPa (109 ksi) 715 MPa (104 ksi)
Предел текучести 570 MPa (83 ksi) 550 MPa (80 ksi)
Удлинение 30 % 35 %

Данные наплавки

Ток 130-220 A
Коэфф. наплавки 4.2-10. lb/h
Коэфф. наплавки 1.9-4.6 kg/h
Диаметр 0.045 in.
Диаметр 1.2 mm
В 24-29 V
Скорость подачи проволоки 228-567 in./min
Скорость подачи проволоки 5.8-14.4 m/min

Классификации

Weld Metal SFA/AWS A5.22 : E309LMoT1-1
SFA/AWS A5.22 : E309LMoT1-4
JIS Z 3323 : TS309LMo-FB1
KS D 3612 : YF309MoLC
EN ISO 17633-A : T 23 12 2 L P C1 2
EN ISO 17633-A : T 23 12 2 L P M21 2

Характеристики расходного материала

Тип сплава C Cr Ni Mo
Защитный газ M21, C1 (EN ISO 14175)
Сварочный ток DC+

Хим. состав наплавленного металла

Хим. состав наплавленного металла
C Cr Mn Mo Ni P S Si
C1 Shielding Gas
0.029 % 22.9 % 1.0 % 2.60 % 12.7 % 0.024 % 0.008 %
C1 shielding gas
0.70 %
M21 Shielding Gas
0.030 % 23.5 % 1.2 % 2.60 % 13.0 % 0.024 % 0.008 % 0.75 %