Exaton 25.10.4.LB is a high alloyed chromium-nickel-molybdenum-nitrogen covered electrode with basic coating for welding of 25%Cr- and superduplex stainless steels (e.g. Sandvik SAF 2507 and Zeron 100).The basic type of electrode combines good welding properties in all positions with high impact strength at low temperatures. The weld metal is characterized by high strength and very good corrosion resistance.Exaton 25.10.4.LB is used for welding of super duplex stainless steels in service temperatures up to 280°C (536°F), where good impact strength at temperatures down to -50°C is required. Common steel types include: ISO 1.4410, 1.4501 and 1.4507. UNS: S32750, S32760, S31260 and S32550. It can also be used as overmatching consumable for 21-23%Cr duplex stainless steels.The weld metals produced are not completely porosity free, but they fulfil the welding requirements described in ASME IX, Article 1 Welding Requirements- QW 191.1.

Загрузка...

Описание

 

Exaton 25.10.4.LB is a high alloyed chromium-nickel-molybdenum-nitrogen covered electrode with basic coating for welding of 25%Cr- and superduplex stainless steels (e.g. Sandvik SAF 2507 and Zeron 100).The basic type of electrode combines good welding properties in all positions with high impact strength at low temperatures. The weld metal is characterized by high strength and very good corrosion resistance.Exaton 25.10.4.LB is used for welding of super duplex stainless steels in service temperatures up to 280°C (536°F), where good impact strength at temperatures down to -50°C is required. Common steel types include: ISO 1.4410, 1.4501 and 1.4507. UNS: S32750, S32760, S31260 and S32550. It can also be used as overmatching consumable for 21-23%Cr duplex stainless steels.The weld metals produced are not completely porosity free, but they fulfil the welding requirements described in ASME IX, Article 1 Welding Requirements- QW 191.1.

 

Типичные свойства образца с V-образным надрезом по Шарпи

после сварки iso

Механические свойства при растяжении

Защитный газ Предел прочности при растяжении Предел текучести Состояние Удлинение
ISO 915 MPa (133 ksi) 750 MPa (109 ksi) После сварки 26 %

Данные наплавки

Ток Время горения электрода при 90% от макс. Тока Производительность наплавки при токе 90% от максимального Диаметр КПД, % Кол-во электродов/кг наплавл. Металла В
50-80 A 50.2 sec 0.72 kg/h (1.6 lb/h) 2.5 x 300.0 mm (0.098 x 11.8 in.) 62 % 100 22 V
70-100 A 58.67 sec 1.2 kg/h (2.6 lb/h) 3.2 x 350.0 mm (1/8 x 13.8 in.) 65 % 53 23 V
100-150 A 2.0 kg/h (4.4 lb/h) 4.0 x 350.0 mm (5/32 x 13.8 in.) 73 % 26

Классификации

Классификации Werkstoffnummer : (1.4410)
SFA/AWS A5.4 : E2594-15
EN ISO 3581-A : E 25 9 4 N L B

Одобрения

Класс EN 13479
Общество CE
Одобрения на материалы выдаются с привязкой к заводу изготовителю. Подробную информацию можно получить в представительствах ESAB.

Характеристики расходного материала

Тип сплава Austenitic-Ferritic CrNiMo
Тип покрытия Basic
Содержание ферритной фазы FN 35-55
Сварочный ток DC+