24.13.LNb is a niobium-stabilized overalloyed filler metal suitable for overlay welding of carbon and low alloy steels, where a type 347 of overlay is required in one layer. Typical applications is cladding of shells and inlets of hydrocrackers, which has a service temperature of 600-650°C. It is used for MIG/MAG welding as well as for overlay welding using hot wire TIG and mechanical TIG.

Загрузка...

Описание

24.13.LNb is a niobium-stabilized overalloyed filler metal suitable for overlay welding of carbon and low alloy steels, where a type 347 of overlay is required in one layer. Typical applications is cladding of shells and inlets of hydrocrackers, which has a service temperature of 600-650°C. It is used for MIG/MAG welding as well as for overlay welding using hot wire TIG and mechanical TIG.



Типичные свойства образца с V-образным надрезом по Шарпи

после сварки

Механические свойства при растяжении

Предел прочности при растяжении Предел текучести Состояние Удлинение
670 MPa (97 ksi) 500 MPa (73 ksi) После сварки 29 %

Данные наплавки

Current Voltage Диаметр проволоки Wire Feed Speed
60-220 A 15-28 V 1.0 mm (0.040 in.) 4.0-12.0 m/min (157-472 in./min)
150-260 A 24-29 V 1.2 mm (0.047 in.) 3.0-10.0 m/min (118-394 in./min)

Классификации

Wire Electrode SFA/AWS A5.9 : ER 309LNb
EN ISO 14343-A : G 23 12 Nb

Характеристики расходного материала

Тип сплава Austenitic (with approx. 15 % ferrite) 24 % Cr — 13 % Ni — Low C — Nb
Защитный газ M12, M13 (EN ISO 14175)

Хим. состав наплавленного металла

Хим. состав проволоки
C Co Cr Cu FN deLong Mn Mo N Nb Ni P S Si Ti
0.01 % 0.02 % 24 % 0.01 % 2.1 % 0.02 % 0.05 % 0.8 % 12.5 % 0.013 % 0.001 % 0.3 % 0.005 %
Хим. состав наплавленного металла
0.02 % 0.02 % 23.2 % 0.01 % 13 % 2.2 % 0.01 % 0.07 % 0.8 % 12.5 % 0.012 % 0.001 % 0.2 %