24.13.LHF welding wire is used for MIG/MAG welding. It is particularly suitable for overlay welding and joining dissimilar steels, for example austenitic stainless steels to low alloyed or non alloyed steels. It has excellent resistance to hot cracking due to its enhanced ferrite content.

Загрузка...

Описание

24.13.LHF welding wire is used for MIG/MAG welding. It is particularly suitable for overlay welding and joining dissimilar steels, for example austenitic stainless steels to low alloyed or non alloyed steels. It has excellent resistance to hot cracking due to its enhanced ferrite content.



Типичные свойства образца с V-образным надрезом по Шарпи

после сварки

Механические свойства при растяжении

Предел прочности при растяжении Предел текучести Состояние Удлинение
610 MPa (88 ksi) 450 MPa (65 ksi) После сварки 30 %

Данные наплавки

Current 150-260 A
Voltage 24-29 V
Диаметр проволоки 0.047 in.
Диаметр проволоки 1.2 mm
Wire Feed Speed 118-394 in./min
Wire Feed Speed 3.0-10.0 m/min

Классификации

Wire Electrode EN ISO 14343-A : G 23 12 L
SFA/AWS A5.9 : ER309L

Одобрения

Одобрения CE EN 13479
VdTÜV 02103
Одобрения на материалы выдаются с привязкой к заводу изготовителю. Подробную информацию можно получить в представительствах ESAB.

Характеристики расходного материала

Тип сплава Austenitic (with approx. 14 % ferrite) 24 % Cr — 13 % Ni — Low C
Защитный газ M12, M13 (EN ISO 14175)

Хим. состав наплавленного металла

Хим. состав проволоки
C Co Cr Cu FN WRC FN deLong Mn Mo N Nb Ni P S Si Ti V
0.01 % 0.03 % 23.5 % 0.03 % 13 % 14 % 1.8 % 0.04 % 0.05 % 0.03 % 13.4 % 0.011 % 0.001 % 0.4 % 0.004 % 0.05 %
Хим. состав наплавленного металла
0.02 % 0.03 % 23.6 % 0.01 % 11 % 12 % 1.7 % 0.02 % 0.07 % 0.01 % 13.4 % 0.013 % 0.001 % 0.3 % 0.03 %