24.13.L is suitable for joining stainless Cr-Ni steels of the 309 type, Cr-steels and dissimilar steels e.g. austenitic stainless steel to carbon or low-alloyed steels for service up to 320°C (610°F). Widely used as barrier layer between carbon/low alloy steel and different stainless grades in cladding operations. It is used for TIG-welding.

Загрузка...

Описание

24.13.L is suitable for joining stainless Cr-Ni steels of the 309 type, Cr-steels and dissimilar steels e.g. austenitic stainless steel to carbon or low-alloyed steels for service up to 320°C (610°F). Widely used as barrier layer between carbon/low alloy steel and different stainless grades in cladding operations. It is used for TIG-welding.



Типичные свойства образца с V-образным надрезом по Шарпи

после сварки

Механические свойства при растяжении

Предел прочности при растяжении Предел текучести Состояние Удлинение
610 MPa (88 ksi) 500 MPa (73 ksi) После сварки 32 %

Классификации

Wire Electrode SFA/AWS A5.9 : ER309L
EN ISO 14343-A : W 23 12 L
Werkstoffnummer : 1.4332

Одобрения

Класс EN 13479
Общество CE
Одобрения на материалы выдаются с привязкой к заводу изготовителю. Подробную информацию можно получить в представительствах ESAB.

Характеристики расходного материала

Тип сплава Austenitic (with approx. 9 % ferrite) 24 % Cr — 13 % Ni — Low C
Защитный газ I1 (EN ISO 14175)

Хим. состав наплавленного металла

Хим. состав наплавленного металла
C Co Cr Cu FN WRC-92 Mn Mo N Nb Ni P S Si V
0.01 % 0.03 % 23.5 % 0.04 % 12 % 1.67 % 0.04 % 0.08 % 0.01 % 13 % 0.018 % 0.014 % 0.40 % 0.03 %
Хим. состав проволоки
&lt.0.02 % 23.5 % &lt.0.1 % 10 % 1.8 % &lt.0.1 % 0.08 % 13.5 % 0.01 % 0.01 % 0.4 %