Exaton 22.8.3.LSi is designed for gas shielded arc welding of duplex stainless steels, such as Sandvik SAF 2205 and Sandvik SAF 2304. Its corrosion resistance is equal to ASTM 904L in most applications. It combines high strength with excellent ductility. Exaton 22.8.3.LSi can also be used for joining Sandvik SAF 2205 or Sandvik SAF 2304 to carbon steel or low-alloy steels. It can be used for plasma welding and overlay welding using hot wire TIG and mechanical TIG.

Загрузка...

Описание

Exaton 22.8.3.LSi is designed for gas shielded arc welding of duplex stainless steels, such as Sandvik SAF 2205 and Sandvik SAF 2304. Its corrosion resistance is equal to ASTM 904L in most applications. It combines high strength with excellent ductility. Exaton 22.8.3.LSi can also be used for joining Sandvik SAF 2205 or Sandvik SAF 2304 to carbon steel or low-alloy steels. It can be used for plasma welding and overlay welding using hot wire TIG and mechanical TIG.



Типичные свойства образца с V-образным надрезом по Шарпи

после сварки

Механические свойства при растяжении

Предел прочности при растяжении Предел текучести Состояние Удлинение
770 MPa (112 ksi) 550 MPa (80 ksi) После сварки 30 %

Данные наплавки

Current Voltage Диаметр проволоки Wire Feed Speed
40-120 A 15-19 V 0.8 mm (0.030 in.) 4.0-8.0 m/min (157-315 in./min)
60-220 A 15-28 V 1.0 mm (0.040 in.) 4.0-12.0 m/min (157-472 in./min)
150-260 A 24-29 V 1.2 mm (0.047 in.) 3.0-10.0 m/min (118-394 in./min)

Классификации

Wire Electrode SFA/AWS A5.9 : ER2209
EN ISO 14343-A : 22 9 3 N L
EN ISO 14343-B : 2209

Одобрения

Одобрения CE EN 13479
VdTÜV 04620
Одобрения на материалы выдаются с привязкой к заводу изготовителю. Подробную информацию можно получить в представительствах ESAB.

Характеристики расходного материала

Тип сплава Austenitic-ferritic (duplex) with approx. 55 FN ferrite — 22.5% Cr — 8% Ni — 3% Mo — Low C + Si
Защитный газ M12, M13 (EN ISO 14175)

Хим. состав наплавленного металла

Хим. состав наплавленного металла
C Co Cr Cu FN WRC-92 Mn Mo N Nb Ni P PRE S Si Ti V W
0.01 % 23 % 0.1 % 54 % 1.5 % 3.1 % 0.16 % 0.01 % 8.5 % 0.02 % 35.8 % 0.001 % 0.8 % 0.01 %
Хим. состав проволоки
0.012 % 0.04 % 23 % 0.09 % 55 % 1.5 % 3.2 % 0.15 % 0.01 % 8.6 % 0.018 % 37 % 0.0007 % 0.8 % 0.003 % 0.05 % 0.01 %