Exaton 22.8.3.LSi is designed for gas shielded arc welding of duplex stainless steels, such as Sandvik SAF 2205 and Sandvik SAF 2304. Its corrosion resistance is equal to ASTM 904L in most applications. It combines high strength with excellent ductility. Exaton 22.8.3.LSi can also be used for joining Sandvik SAF 2205 or Sandvik SAF 2304 to carbon steel or low-alloy steels.

Загрузка...

Описание

Exaton 22.8.3.LSi is designed for gas shielded arc welding of duplex stainless steels, such as Sandvik SAF 2205 and Sandvik SAF 2304. Its corrosion resistance is equal to ASTM 904L in most applications. It combines high strength with excellent ductility. Exaton 22.8.3.LSi can also be used for joining Sandvik SAF 2205 or Sandvik SAF 2304 to carbon steel or low-alloy steels.



Типичные свойства образца с V-образным надрезом по Шарпи

после сварки

Механические свойства при растяжении

Предел прочности при растяжении Предел текучести Состояние Удлинение
710 MPa (103 ksi) 580 MPa (84 ksi) После сварки 28 %

Классификации

Wire Electrode SFA/AWS A5.9 : ER2209
EN ISO 14343-A : W 22 9 3 N L
EN ISO 14343-B : 2209

Одобрения

Одобрения CE EN 13479
VdTÜV 10055
Одобрения на материалы выдаются с привязкой к заводу изготовителю. Подробную информацию можно получить в представительствах ESAB.

Характеристики расходного материала

Тип сплава Austenitic-ferritic (duplex) with approx. 55 FN ferrite — 22.5% Cr — 8% Ni — 3% Mo — Low C + Si
Защитный газ I1, I3, N2 (EN ISO 14175)

Хим. состав наплавленного металла

Хим. состав наплавленного металла
C Co Cr Cu FN WRC-92 Mn Mo N Nb Ni P PRE S Si Ti V W
0.01 % 23 % 0.1 % 54 % 1.5 % 3.1 % 0.16 % 0.01 % 8.5 % 0.02 % 35.8 % 0.001 % 0.8 % 0.01 %
Хим. состав проволоки
0.012 % 0.04 % 23 % 0.09 % 55 % 1.5 % 3.2 % 0.15 % 0.01 % 8.6 % 0.018 % 37 % 0.0007 % 0.8 % 0.003 % 0.05 % 0.01 %