Exaton 19.9.LSi is a filler metal particularly suited for MIG welding but can also be used for TIG and plasma arc welding. It is suitable for joining stainless steels of the 18Cr/8Ni ELC-type and 18Cr/8Ni/Nb type for service temperatures up to 350°C (660°F). It is used for TIG-welding.

Загрузка...

Описание

Exaton 19.9.LSi is a filler metal particularly suited for MIG welding but can also be used for TIG and plasma arc welding. It is suitable for joining stainless steels of the 18Cr/8Ni ELC-type and 18Cr/8Ni/Nb type for service temperatures up to 350°C (660°F). It is used for TIG-welding.



Типичные свойства образца с V-образным надрезом по Шарпи

после сварки

Механические свойства при растяжении

Состояние После сварки После сварки
Предел прочности при растяжении 600 MPa (87 ksi) 440 MPa (64 ksi)
Предел текучести 390 MPa (57 ksi) 290 MPa (42 ksi)
Удлинение 42 % 24 %

Классификации

Wire Electrode SFA/AWS A5.9 : ER308LSi
EN ISO 14343-A : W 19 9 L Si
Werkstoffnummer : 1.4316

Одобрения

Одобрения CE EN 13479
DB 43.118.01
VdTÜV 00869
Одобрения на материалы выдаются с привязкой к заводу изготовителю. Подробную информацию можно получить в представительствах ESAB.

Характеристики расходного материала

Тип сплава Austenitic (with approx. 8 % ferrite) 19% Cr — 9% Ni — Low C — High Si
Защитный газ I1 (EN ISO 14175)

Хим. состав наплавленного металла

Хим. состав проволоки
C Co Cr Cu FN WRC-92 Mn Mo N Nb Ni P S Si Ti
0.013 % 0.10 % 20 % 0.2 % 9 % 1.8 % 0.2 % 0.06 % 0.01 % 10 % 0.021 % 0.011 % 0.9 % 0.004 %
Хим. состав наплавленного металла
0.02 % 19.6 % 0.13 % 8 % 1.7 % 0.02 % 0.06 % 0.01 % 10.3 % 0.020 % 0.010 % 0.7 %