19.12.3.L is used for welding of austenitic stainless alloys of 18% Cr — 8% Ni and 18% Cr — 10% Ni — 3% Mo-types, stabilized or non-stabilized, e.g. ASTM 316, 316L and 316Ti as well as 304, 304L, 321 and 347, used for service temperatures up to 400°C (750°F). It is also used for Cr steels with max. 19% Cr.It is used for TIG-welding.

Загрузка...

Описание

19.12.3.L is used for welding of austenitic stainless alloys of 18% Cr — 8% Ni and 18% Cr — 10% Ni — 3% Mo-types, stabilized or non-stabilized, e.g. ASTM 316, 316L and 316Ti as well as 304, 304L, 321 and 347, used for service temperatures up to 400°C (750°F). It is also used for Cr steels with max. 19% Cr.It is used for TIG-welding.



Типичные свойства образца с V-образным надрезом по Шарпи

после сварки

Механические свойства при растяжении

Предел прочности при растяжении Предел текучести Состояние Удлинение
610 MPa (88 ksi) 500 MPa (73 ksi) После сварки 39 %

Классификации

Wire Electrode SFA/AWS A5.9 : ER316L
EN ISO 14343-A : W 19 12 3 L
Werkstoffnummer : 1.4430

Одобрения

Одобрения CE EN 13479
DNV-GL VL 316L
VdTÜV 00066
Одобрения на материалы выдаются с привязкой к заводу изготовителю. Подробную информацию можно получить в представительствах ESAB.

Характеристики расходного материала

Тип сплава Austenitic (with appr. 8 % ferrite) 19 % Cr — 12 % Ni — 3 % Mo — Low C
Защитный газ I1 (EN ISO 14175)

Хим. состав наплавленного металла

Хим. состав проволоки
C Cr Cu FN WRC-92 Mn Mo N Nb Ni P S Si
0.015 % 18.5 % 0.1 % 9 % 1.7 % 2.6 % 0.04 % 0.02 % 12 % &lt.0.025 % 0.015 % 0.4 %
Хим. состав наплавленного металла
&lt.0.02 % 18 % 0.1 % 7 % 1.7 % 2.5 % 0.05 % 0.01 % 12 % &lt.0.03 % &lt.0.02 % 0.4 %