Description
Exaton Ni72HP is filler material for joining NiCrFe alloys, 9% Ni steels used at cryogenic temperatures, stainless steels to carbon steels, high service temperature NiCu alloys to carbon steels and NiCu alloys to nickel alloys. Exaton Ni72HP can be used in air up to 1175°C (2145°F) and in sulphur dioxide atmospheres up to 800°C (1470°F). It is used for MIG/MAG welding.
Механические свойства при растяжении
| Предел прочности при растяжении |
Предел текучести |
Состояние |
Удлинение |
| 660 MPa (96 ksi) |
420 MPa (61 ksi) |
После сварки |
35 % |
Данные наплавки
| Current |
Voltage |
Диаметр проволоки |
Wire Feed Speed |
|
| 40-120 A |
15-19 V |
0.8 mm (0.030 in.) |
4.0-8.0 m/min (157-315 in./min) |
| 60-220 A |
15-28 V |
1.0 mm (0.040 in.) |
4.0-12.0 m/min (157-472 in./min) |
| 150-260 A |
24-29 V |
1.2 mm (0.047 in.) |
3.0-10.0 m/min (118-394 in./min) |
| 230-350 A |
25-30 V |
1.6 mm (1/16 in.) |
3.0-5.0 m/min (118-197 in./min) |
Классификации
| Wire Electrode |
SFA/AWS A5.14 : ERNiCr-3
EN ISO 18274 : S Ni 6082 (NiCr20Mn3Nb) |
Одобрения
| Одобрения |
CE EN 13479
VdTÜV 00073 |
| Одобрения на материалы выдаются с привязкой к заводу изготовителю. Подробную информацию можно получить в представительствах ESAB. |
Хим. состав наплавленного металла
| Хим. состав проволоки |
| Al |
C |
Co |
Cr |
Cu |
Fe |
Mn |
Mo |
N |
Nb |
Nb+Ta |
Ni |
P |
S |
Si |
Ti |
| 0.4 % |
<.=0.03 % |
<.=0.1 % |
20.0 % |
<.=0.05 % |
<.=1 % |
3 % |
≤0.05 % |
<.=0.05 % |
2.5 % |
2.6 % |
73 % |
<.=0.01 % |
<.=0.01 % |
0.1 % |
0.4 % |
| Хим. состав наплавленного металла |
| — |
<.0.02 % |
<.0.02 % |
20 % |
0.01 % |
≤1 % |
3.2 % |
0.01 % |
0.03 % |
2.2 % |
2.5 % |
73 % |
<.0.003 % |
0.003 % |
0.01 % |
0.4 % |