Description
24.13.L is suitable for joining stainless Cr-Ni steels of the 309 type, Cr-steels and dissimilar steels e.g. austenitic stainless steel to carbon or low-alloyed steels for service up to 320°C (610°F). It is used for MIG/MAG welding. Widely used as barrier layer between carbon/low alloy steel and different stainless grades in cladding operations.
Механические свойства при растяжении
| Предел прочности при растяжении |
Предел текучести |
Состояние |
Удлинение |
| 590 MPa (86 ksi) |
440 MPa (64 ksi) |
После сварки |
32 % |
Данные наплавки
| Current |
Voltage |
Диаметр проволоки |
Wire Feed Speed |
|
| 40-120 A |
15-19 V |
0.8 mm (0.030 in.) |
4.0-8.0 m/min (157-315 in./min) |
| 60-220 A |
15-28 V |
1.0 mm (0.040 in.) |
4.0-12.0 m/min (157-472 in./min) |
| 150-260 A |
24-29 V |
1.2 mm (0.047 in.) |
3.0-10.0 m/min (118-394 in./min) |
| 230-350 A |
25-30 V |
1.6 mm (1/16 in.) |
3.0-5.0 m/min (118-197 in./min) |
Классификации
| Wire Electrode |
EN ISO 14343-A : G 23 12 L
SFA/AWS A5.9 : ER309L
Werkstoffnummer : 1.4332 |
Одобрения
| Класс |
EN 13479 |
| Общество |
CE |
| Одобрения на материалы выдаются с привязкой к заводу изготовителю. Подробную информацию можно получить в представительствах ESAB. |
Характеристики расходного материала
| Тип сплава |
Austenitic (with approx. 9 % ferrite) 24 % Cr — 13 % Ni — Low C |
| Защитный газ |
M12, M13 (EN ISO 14175) |
Хим. состав наплавленного металла
| Хим. состав наплавленного металла |
| C |
Co |
Cr |
Cu |
FN WRC-92 |
Mn |
Mo |
N |
Nb |
Ni |
P |
S |
Si |
V |
| 0.01 % |
0.03 % |
23.6 % |
0.04 % |
12 % |
1.67 % |
0.01 % |
0.08 % |
0.01 % |
13.5 % |
0.018 % |
0.016 % |
0.40 % |
0.03 % |
| Хим. состав проволоки |
| <.0.02 % |
— |
23.5 % |
<.0.1 % |
10 % |
1.8 % |
<.0.1 % |
0.08 % |
— |
13.5 % |
0.01 % |
0.01 % |
0.4 % |
— |