Description
Exaton 15W is a basic welding flux for submerged arc welding giving good slag removal and a fine bead appearance. Its relatively high basicity makes it suitable for joining of austenitic and duplex stainless steel when high impact strength is desired. Due to its low niobium content burn-off it can be used advantageously with stabilized wire electrodes.Exaton 15W is a high performance welding flux in many joining applications in the chemical, petrochemical and oil&.gas industry. It is particularly suited for Exaton range of duplex wire electrodes (e.g. 22.8.3.L/25.10.4.L) due to the highly neutral behavior, which ensures an optimal balanced microstructure.Taking the benefit of its features (not limited to nice bead appearance and self slag release only), it can also be used in combination with NiCrMo-3 wire for several other applications (i.e. both joining and weld overlay).
Классификации
| Класс | S A AF 2 |
| Название | EN ISO 14174 |
Характеристики расходного материала
| Показатель щелочности | nom: 1.9 |
| Плотность | nom: 1.0 Kg/l |
| Тип шлака | Fluoride basic CaF2-Al2O3-SiO2 |
| Сварочный ток | 1200 A (Using 60×0.5 mm strip) |
Расход флюса
| В | кг флюс / кг проволока DC+ |
| 26 V | 0.5 kg |
| 30 V | 0.6 kg |
| 34 V | 0.8 kg |
| 38 V | 1.0 kg |
| Ток | Габаритные размеры | Скорость перемещения |
| 580 A | 4.0 mm | 33 m/h |
Классификации
| Проволока | AWS/EN |
| Exaton 19.9.Nb | A5.9:ER347/ 14343-A:S 19 9 Nb |
| Exaton Ni56 | A5.14:ERNiCrMo-4/ 18274:S Ni 6276 (NiCr15Mo16Fe6W4) |
| Exaton 25.10.4.L | A5.9:ER2594/ 14343-A:S 25 9 4 N L |
| Exaton Ni60 SAW | A5.14:ERNiCrMo-3/ 18274:S Ni 6625 (NiCr22Mo9Nb) |
| Exaton 19.12.3.L | A5.9:ER316L/ 14343-A:S 19 12 3 L |
| Exaton 19.9.L | A5.9:ER308L/ 14343-A:S 19 9 L |
| Exaton 20.25.5.LCu | A5.9:ER385/ 14343-A:S 20 25 5 Cu L |
| Exaton 22.15.3.L | A5.9:ER(309LMo)/ 14343-A:S 23 12 2 L |
| Exaton 22.8.3.L | A5.9:ER2209/ 14343-A:S 22 9 3 N L |
| Exaton 24.13.LHF | A5.9:ER309L/ 14343-A:S 23 12 L |
| Exaton 24.13.LNb | A5.9:ER”309LNb”/ 14343-A:S 23 12 Nb |
| Exaton 24.13.L | A5.9:ER309L/ 14343-A:S 23 12 L |
| Exaton 27.31.4.LCu | A5.9:ER383/ 14343-A:S 27 31 4 Cu L |
| Exaton 19.9.Nb HF | A5.9:ER347/ 14343-A:S 19 9 Nb |
| Exaton 22.12.HT | 14343-A:S 21 10 N |
| Exaton 25.22.2.LMn | A5.9:ER»310LMo»/ 14343-A:S 25 22 2 N L |
Одобрения
| Проволока | BV | DNV-GL | VdTÜV |
| Exaton 19.12.3.L | — | — | * |
| Exaton 19.9.L | — | — | * |
| Exaton 22.8.3.L | * | * | * |
| Exaton 25.10.4.L | * | * | * |
| Применимо для определенных производственных подразделений. Свяжитесь с ЭСАБ для получения более подробной информации. Для загрузки информационного бюллетеня по комбинации флюс/проволока посетите esab.com |
Типичные механические свойства
| Проволока | Состояние | Предел текучести | Предел прочности при растяжении | Ударная вязкость по Шарпи, V-образный надрез | Удлинение |
| Exaton 19.12.3.L | После сварки null | 390 MPa (57 ksi) |
530 MPa (77 ksi) |
100 J @ 20°C, (74 ft-lb @ 68 °F) 85 J @ -40°C, (63 ft-lb @ -40 °F) 40 J @ -196°C, (30 ft-lb @ -320.8 °F) |
41 % |
| Exaton 19.9.L | После сварки null | 390 MPa (57 ksi) |
560 MPa (81 ksi) |
90 J @ 20°C, (67 ft-lb @ 68 °F) 35 J @ -196°C, (26 ft-lb @ -320.8 °F) |
35 % |
| Exaton 19.9.Nb | После сварки null | 470 MPa (68 ksi) |
650 MPa (94 ksi) |
80 J @ 20°C, (59 ft-lb @ 68 °F) |
32 % |
| Exaton 19.9.Nb HF | После сварки DC+ | 440 MPa (64 ksi) |
610 MPa (88 ksi) |
75 J @ 20°C, (56 ft-lb @ 68 °F) |
32 % |
| Exaton 20.25.5.LCu | После сварки null | 345 MPa (50 ksi) |
550 MPa (80 ksi) |
125 J @ 20°C, (93 ft-lb @ 68 °F) 100 J @ -196°C, (74 ft-lb @ -320.8 °F) |
40 % |
| Exaton 22.12.HT | После сварки null | 400 MPa (58 ksi) |
580 MPa (84 ksi) |
120 J @ 20°C, (89 ft-lb @ 68 °F) |
35 % |
| Exaton 22.15.3.L | После сварки null | 400 MPa (58 ksi) |
600 MPa (87 ksi) |
140 J @ 20°C, (104 ft-lb @ 68 °F) |
40 % |
| Exaton 22.8.3.L | После сварки null | 650 MPa (94 ksi) |
790 MPa (115 ksi) |
115 J @ 20°C, (85 ft-lb @ 68 °F) 85 J @ -40°C, (63 ft-lb @ -40 °F) |
33 % |
| Exaton 24.13.L | После сварки null | 400 MPa (58 ksi) |
600 MPa (87 ksi) |
140 J @ 20°C, (104 ft-lb @ 68 °F) |
40 % |
| Exaton 24.13.LHF | После сварки null | 410 MPa (59 ksi) |
600 MPa (87 ksi) |
140 J @ 20°C, (104 ft-lb @ 68 °F) |
40 % |
| Exaton 24.13.LNb | После сварки null | 400 MPa (58 ksi) |
600 MPa (87 ksi) |
90 J @ 20°C, (67 ft-lb @ 68 °F) |
35 % |
| Exaton 25.10.4.L | После сварки DC+ | 690 MPa (100 ksi) |
880 MPa (128 ksi) |
90 J @ 20°C, (67 ft-lb @ 68 °F) 60 J @ -40°C, (44 ft-lb @ -40 °F) |
25 % |
| Exaton 25.22.2.LMn | После сварки DC+ | 335 MPa (49 ksi) |
575 MPa (83 ksi) |
120 J @ 20°C, (89 ft-lb @ 68 °F) |
42 % |
| Exaton 27.31.4.LCu | После сварки null | 360 MPa (52 ksi) |
540 MPa (78 ksi) |
165 J @ 20°C, (122 ft-lb @ 68 °F) |
35 % |
| Exaton Ni56 | После сварки HI 1.6-1.8 kJ/mm DC+ | 450 MPa (65 ksi) |
700 MPa (102 ksi) |
100 J @ -60°C, (74 ft-lb @ -76 °F) 80 J @ -196°C, (59 ft-lb @ -320.8 °F) 100 J @ -60°C, (59 ft-lb @ -320.8 °F) |
45 % |
| Exaton Ni60 SAW | После сварки null | 445 MPa (65 ksi) |
715 MPa (104 ksi) |
93 J @ -60°C, (69 ft-lb @ -76 °F) 82 J @ -196°C, (61 ft-lb @ -320.8 °F) |
45 % |
Хим. состав наплавленного металла
| Хим. состав наплавленного металла | ||||||||||||||||||
| C | Co | Cr | Cu | FN WRC | FN WRC-92 | FN deLong | Fe | Mn | Mo | N | Nb | Nb+Ta | Ni | P | S | Si | V | W |
| Exaton 19.12.3.L | ||||||||||||||||||
| 0.01 % | — | 18.1 % | — | — | — | — | — | 1.5 % | 2.6 % | — % | — | — | 12.3 % | — % | — % | 0.5 % | — | — |
| Exaton 19.9.L | ||||||||||||||||||
| 0.02 % | 0.1 % | 19.5 % | 0.1 % | — | 6 % | — | — | 1.2 % | 0.15 % | 0.05 % | — | — | 10 % | 0.025 % | 0.012 % | 0.6 % | — | — |
| Exaton 19.9.Nb HF | ||||||||||||||||||
| 0.04 % | — | 19.4 % | 0.11 % | 12 % | — | 13 % | — | 1.4 % | 0.12 % | 0.04 % | 0.7 % | 0.7 % | 9.3 % | 0.02 % | 0.01 % | 0.66 % | — | — |
| Exaton 19.9.Nb | ||||||||||||||||||
| 0.03 % | 0.1 % | 18.7 % | 0.10 % | 5 % | — | 6 % | — | 0.9 % | 0.03 % | 0.05 % | 0.5 % | 0.6 % | 9.5 % | 0.018 % | 0.013 % | 0.5 % | — | — |
| Exaton 20.25.5.LCu | ||||||||||||||||||
| 0.01 % | — | 19.6 % | — % | — | — | — | — | 1.4 % | 4.5 % | — | — | — | 25 % | — % | — % | 0.5 % | — | — |
| Exaton 22.8.3.L | ||||||||||||||||||
| 0.01 % | — | 22.6 % | — | — | — | — | — | 1.2 % | 3.1 % | 0.15 % | — | — | 8.6 % | — % | — % | 0.7 % | — | — |
| Exaton 24.13.LNb | ||||||||||||||||||
| <.=0.020 % | — | 23.5 % | — | — | — | — | — | 1.2 % | — | — | 0.7 % | — | 12 % | <.=0.025 % | <.=0.015 % | 0.7 % | — | — |
| Exaton 25.10.4.L | ||||||||||||||||||
| <.=0.020 % | — | 24.5 % | — | — | — | — | — | 0.3 % | 4 % | 0.21 % | — | — | 9.6 % | <.=0.020 % | <.=0.015 % | 0.6 % | — | — |
| Exaton 25.22.2.LMn Current: DC+, 420A, 27V | ||||||||||||||||||
| 0.02 % | — | 24.5 % | 0.1 % | — | — | — | — | 4.0 % | 2.1 % | 0.12 % | — | — | 22.0 % | — | — | 0.1 % | — | — |
| Exaton 27.31.4.LCu | ||||||||||||||||||
| 0.01 % | — | 26.3 % | 1.0 % | — | — | — | — | 1.4 % | 3.5 % | 0.06 % | — | — | 31.3 % | 0.01 % | 0.003 % | 0.4 % | — | — |
| Exaton Ni56 DC+ | ||||||||||||||||||
| 0.01 % | 0.1 % | 15.1 % | — | — | — | — | 6.8 % | 0.4 % | 15.6 % | — | — | — | Bal % | — | — | 0.20 % | 0.1 % | 3.6 % |
| Exaton Ni60 SAW Current: DC+, 400A, 28V, travel speed: 25 m/h. | ||||||||||||||||||
| 0.02 % | — | 22 % | 0.1 % | — | — | — | 5 % | 0.2 % | 9 % | — | — | 3 % | — | 0.015 % | 0.005 % | 0.4 % | — | — |